一座投运几年的220kV变电站,铜质材料表面出现了不同程度的腐蚀,经测试分析,其腐蚀原因为硫化氢气体腐蚀。提出了解决腐蚀的对策,可供解决这类实际问题时参考。
In a substation that has operated for a few years, more or less erosion has occurred on the surfaces of all copper materials. The reasons for corrosion were hhydrogen sulfide gas by zhe analyzed and experiments. Put forward to solve the corrosion solution, can be used to solve this kind of problems.