Ti-24Nb-4Zr-8Sn, abbreviated as Ti2448 from its chemical composition in weight percent, is a multifunctional /3 type titanium alloy with body centered cubic （bcc） crystal structure, and its highly localized plastic deformation behavior contributes significantly to grain refinement during conventional cold processing. In the paper, the nanostructured （NS） alloy with grain size less than 50 nm produced by cold rolling has been used to investigate its superplastic deformation behavior by uniaxial tensile tests at initial strain rates of 1.5 ×10-2, 1.5×10^-3 and 1.6×10-4 s-1 and temperatures of 600,650 and 700℃. The results show that, in comparison with the coarse-grained alloy with size of 50 μm, the NS alloy has better superplasticity with elongation up to ～275% and ultimate strength of 50-100 MPa. Strain rate sensitivity （m） of the NS alloy is 0.21, 0.30 and 0.29 for 600,650 and 700℃, respectively. These results demonstrate that grain refinement is a valid way to enhance the superplasticity of Ti2448 alloy.
Ti-24Nb-4Zr-8Sn, abbreviated as Ti2448 from its chemical composition in weight percent, is a multifunctional /3 type titanium alloy with body centered cubic （bcc） crystal structure, and its highly localized plastic deformation behavior contributes significantly to grain refinement during conventional cold processing. In the paper, the nanostructured （NS） alloy with grain size less than 50 nm produced by cold rolling has been used to investigate its superplastic deformation behavior by uniaxial tensile tests at initial strain rates of 1.5 ×10-2, 1.5×10^-3 and 1.6×10-4 s-1 and temperatures of 600,650 and 700℃. The results show that, in comparison with the coarse-grained alloy with size of 50 μm, the NS alloy has better superplasticity with elongation up to ～275% and ultimate strength of 50-100 MPa. Strain rate sensitivity （m） of the NS alloy is 0.21, 0.30 and 0.29 for 600,650 and 700℃, respectively. These results demonstrate that grain refinement is a valid way to enhance the superplasticity of Ti2448 alloy.
基金
supported by the National Natural Science Foundation of China (Nos. 51071152and 50901080)
the National High Technology Research and Development Program of China (No.2011AA030106)