A P-substituted sulfonyl-containing compound was synthesized in the lab. The structure of the compound was demonstrated by 1H and 31P NMR. The propylene polymerization catalysts were prepared by incorporating an internal donor, and the content of Ti, H and C in the catalysts was also checked by elemental analysis. The effect of dosage of the donor, the Al/Ti ratio and the polymerization temperature on the catalyst activity were studied, the results suggested that the dosage of donor, the Al/Ti ratio and the polymerization temperature could affect not only the activity of catalyst but also the isotacticity index of the polymer. A catalyst with high activity was selected, and the polypropylene formed in the presence of this catalyst had high isotacticity index.
A P-substituted sulfonyl-containing compound was synthesized in the lab. The structure of the compound was demonstrated by ^1H and ^31p NMR. The propylene polymerization catalysts were prepared by incorporating an internal donor, and the content of Ti, H and C in the catalysts was also checked by elemental analysis. The effect of dosage of the donor, the Al/Ti ratio and the polymerization temperature on the catalyst activity were studied, the results suggested that the dosage of donor, the Al/Ti ratio and the polymerization temperature could affect not only the activity of catalyst but also the isotacticity index of the polymer. A catalyst with high activity was selected, and the polypropylene formed in the presence of this catalyst had high isotacticity index.
基金
the PetroChina Science & Technology Management Department for the financial support (No.2010F-19)