摘要
用CPE与CaCO3复配制备出高韧性PVC复合材料,研究了CPE、CaCO3对PVC复合材料力学性能的影响。结果表明:CPE能有效提高PVC的冲击强度;CaCO3在一定用量范围内,可以提高PVC的冲击强度;CPE与CaCO3协同增韧,PVC复合材料的冲击强度可达60 kJ/m2,拉伸强度约为37 MPa,断裂伸长率可达65%。
The high toughness PVC composite was prepared by adding CPE and CaCO3 into PVC,and the effects of CaCO3 and CPE on mechanical properties of PVC were studied.The results show that: the impact strength of PVC improves with the using amount of CaCO3 in a certain range;the impact strength of PVC composite reaches to 60 kJ/m^2,the tensile strength is about 37 MPa,and then the elongation at break reaches to 65% while CPE and CaCO3 has synergistic toughening effect on PVC.