摘要
For describing and resolving the process of chromium ore smelting reduction in a converter preferably, the coupling dynamic model was established based on the kinetic models of chromium ore dissolution and interfacial re- ducing reaction between the slag and metal. When 150 t stainless steel crude melts with chromium of 12% are produced in a smelting reduction converter with no initial chromium in metal at 1 560℃, the results of the coupling dynamic model show that the mean reduction rate and injection rate of chromium ore are 0. 091% ·min^-1 and 467 kg · min^-1 , respectively. The foundation of the coupling dynamic model provides a reference and basis on the constitution of rational processing route for a practical stainless steelmaking.
For describing and resolving the process of chromium ore smelting reduction in a converter preferably, the coupling dynamic model was established based on the kinetic models of chromium ore dissolution and interfacial re- ducing reaction between the slag and metal. When 150 t stainless steel crude melts with chromium of 12% are produced in a smelting reduction converter with no initial chromium in metal at 1 560℃, the results of the coupling dynamic model show that the mean reduction rate and injection rate of chromium ore are 0. 091% ·min^-1 and 467 kg · min^-1 , respectively. The foundation of the coupling dynamic model provides a reference and basis on the constitution of rational processing route for a practical stainless steelmaking.
基金
Sponsored by National Natural Science Foundation of China(50904017)
Open Subject Fund of State Key Laboratory of Rolling and Automation of NEU of China(2009003)