摘要
Fracture data of both parent metal and weldment metals from surface cracked tensile plates made of 2219-T87 Al alloy at cryogenic temperatures were correlated using a modified inherent flaw model. Fracture parameters to generate the failure assessment diagram were determined for the material. Fracture analysis was carried out considering the ultimate tensile strength value and the fracture data of aluminium base metal and weldment metal generated from center–surface cracked tensile specimens having different thicknesses. The failure assessment diagram of a material generated from tensile fracture plate configuration can be applied to failure pressure estimation of any cracked component, made of the same material.
将2219-T87铝合金板材进行低温拉伸试验,用改进的固有缺陷模型分析铝合金基材和焊接接头金属表面裂纹试样的断裂强度数据,通过构成的失效评估图来确定材料的断裂参数。通过考虑材料的极限拉伸强度、铝基材及焊接接头金属的断裂强度数据,对具有不同厚度的中心表面裂纹拉伸试样进行断裂分析。由拉伸断裂板材所得到的失效评估图能够应用到由相同材料构成的任何开裂组件的失效压力估计。