摘要
Advantages of the detached phenomena have influenced researchers to modify the conventional methods to promote it on the earth. Since 1994, the vertical directional solidification （VDS） technique has been employed for the growth of bulk crystals, without the seed, without contact to the ampoule wall, without coating and without external pressure. An automated furnace was designed and fabricated for the controlled temperature gradients, growth conditions and parameters. The typical ingots growths of GaSb have shown the gap of 20 μm-145 μm and mobility μn = 1125 cm^2/V.sec at 300 K. Mobility is highest and five times larger than the attached growths. Dislocation density is the order of 104/cm2 in the conical region, decreases in the direction of growth, and in many crystals reached less than 103/cm2. The spontaneous gap formation due to the meniscus depends on the pressure differences and thermal state. GaSb grown ingots have shown progress in the properties of crystal grown ever, and attributed to reduce thermal stress without contact to the ampoule wall.