摘要
New types of polyamides containing pendent triaryl pyridine groups were successfully synthesized by direct polycondensation of a symmetry diamine,（4-（4-（2,6-diphenylpyridin-4yl）phenoxy）phenyl）-3,5-diaminobezamide（DPDAB）, and various aromatic and aliphatic dicarboxylic diacids in NMP using triphenyl phosphate（TPP） and pyridine as catalyst. The diamine and all the prepared polyamides were fully characterized by using FT-IR,~1H-NMR,UV-Vis spectroscopy, fluorimetry and elemental analysis.The inherent viscosity of polyamides ranged from 0.45 dL/g to 0.68 dL/g.All the polymers exhibited solubility in common polar aprotic solvents such as NMP,DMAc,DMF,DMSO,pyridine,HMPA,and even in less polar solvents such as THF and m-cresol at room temperature.Thermal properties of polyamides were evaluated by means of DSC,DMTA and TGA.These polymers showed glass transition temperatures（T_g） in the range of 138-210℃. Their initial decomposition temperature（T_i） varied from 265℃to 310℃under N_2.The dilute solution（0.2 g/dL） of polyamides in DMF exhibited fluorescence emission withλ_（max） in the range of 470-550 nm.
New types of polyamides containing pendent triaryl pyridine groups were successfully synthesized by direct polycondensation of a symmetry diamine,（4-（4-（2,6-diphenylpyridin-4yl）phenoxy）phenyl）-3,5-diaminobezamide（DPDAB）, and various aromatic and aliphatic dicarboxylic diacids in NMP using triphenyl phosphate（TPP） and pyridine as catalyst. The diamine and all the prepared polyamides were fully characterized by using FT-IR,~1H-NMR,UV-Vis spectroscopy, fluorimetry and elemental analysis.The inherent viscosity of polyamides ranged from 0.45 dL/g to 0.68 dL/g.All the polymers exhibited solubility in common polar aprotic solvents such as NMP,DMAc,DMF,DMSO,pyridine,HMPA,and even in less polar solvents such as THF and m-cresol at room temperature.Thermal properties of polyamides were evaluated by means of DSC,DMTA and TGA.These polymers showed glass transition temperatures（T_g） in the range of 138-210℃. Their initial decomposition temperature（T_i） varied from 265℃to 310℃under N_2.The dilute solution（0.2 g/dL） of polyamides in DMF exhibited fluorescence emission withλ_（max） in the range of 470-550 nm.