The reference test methods are carried out parallelly, by means of chemical analysis, X-ray diffraction, differential scanning calorimetry-thermogravimetry, scanning electron microscopy and polarized optical microscope to study the formation of C4A3S in the presence and absence of nucleating agent. The results show that nucleating agent with high calcium and low heat consumption as tricalcium silicate （C3S） promotes the formation of C4A3S and increases desulfurization degree obviously. During calcining raw meals doped with C3S, the grain sizes of C4A3S are larger compared with that without C3S. And at the same calcining level, the mass loss and the heat consumption belonged to CaCO3 decomposition is reduced.
The reference test methods are carried out parallelly, by means of chemical analysis, X-ray diffraction, differential scanning calorimetry-thermogravimetry, scanning electron microscopy and polarized optical microscope to study the formation of C4A3S in the presence and absence of nucleating agent. The results show that nucleating agent with high calcium and low heat consumption as tricalcium silicate （C3S） promotes the formation of C4A3S and increases desulfurization degree obviously. During calcining raw meals doped with C3S, the grain sizes of C4A3S are larger compared with that without C3S. And at the same calcining level, the mass loss and the heat consumption belonged to CaCO3 decomposition is reduced.
作者
GUO Huiling
XIE Junlin
ZHANG Shu
XU Qi
郭惠玲;谢峻林;ZHANG Shu;XU Qi(Key Laboratory for Silicate Materials Science and Engineering of Ministry of Education,Wuhan University of Technology,Wuhan 430070,China)
基金
the National Natural Science Foundation of China (No. 50972116)