Novel red-emitting phosphors Sr2MgSi2O7：Eu3＋ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and fluorescence spectrophotometer, respectively. The results showed that the as-synthesized sample was Sr2MgSi2O7 with tetragonal crystal structure. The excitation spectrum of Sr2MgSi2O7：Eu3＋ was composed of two major parts： one was the broad band between 200 and 350 nm, which belonged to the charge transfer of Eu3＋-O2-; the other consisted of a series of sharp lines between 350 and 450 nm, ascribed to the f-f transition of Eu3＋. The emission spec-trum consisted of two emission peaks at 593 and 616 nm, which was attributed to 5D0→7F1 and 5D0→7F2 of Eu3＋, respectively. The concen-tration of Eu3＋ （x） had great effect on the emission intensity of Sr2-xMgSi2O7：Eu3＋x. When x varied in the range of 0.04-0.18, the intensity of emission peaks at 593 and 616 nm increased gradually with the concentration of Eu3＋ increasing. It was interesting that no concentration quenching occurred. Moreover, the luminescent intensity could be greatly enhanced with incorporation of charge compensator Li＋ ions.
Novel red-emitting phosphors Sr2MgSi2O7：Eu3＋ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and fluorescence spectrophotometer, respectively. The results showed that the as-synthesized sample was Sr2MgSi2O7 with tetragonal crystal structure. The excitation spectrum of Sr2MgSi2O7：Eu3＋ was composed of two major parts： one was the broad band between 200 and 350 nm, which belonged to the charge transfer of Eu3＋-O2-; the other consisted of a series of sharp lines between 350 and 450 nm, ascribed to the f-f transition of Eu3＋. The emission spec-trum consisted of two emission peaks at 593 and 616 nm, which was attributed to 5D0→7F1 and 5D0→7F2 of Eu3＋, respectively. The concen-tration of Eu3＋ （x） had great effect on the emission intensity of Sr2-xMgSi2O7：Eu3＋x. When x varied in the range of 0.04-0.18, the intensity of emission peaks at 593 and 616 nm increased gradually with the concentration of Eu3＋ increasing. It was interesting that no concentration quenching occurred. Moreover, the luminescent intensity could be greatly enhanced with incorporation of charge compensator Li＋ ions.
基金
Project supported by the National Natural Science Foundation of China (20675023)