The kinetics of recrystallization for twin-roll casting AZ31 magnesium alloy with different thicknesses during homogenization was analyzed.It is shown that fine grains are first formed at the boundaries of deformed bands in the twin-roll casting slab.The recrystallized grains with no strain are gradually substituted for the deformed microstructure of twin-roll casting AZ31 magnesium alloy.The incubation temperature and time for the recrystallization of a twin-roll casting AZ31 magnesium alloy strip with a thickness of 3 mm are lower and shorter than those of the 6-mm thick strip,respectively.The 3-mm thick twin-roll casting magnesium alloy has finer grains than the 6-mm thick strip.The activation energies of recrystallization for twin-roll casting AZ31 magnesium alloy slabs with the thickness of 3 and 6 mm are 88 and 69 kJ/mol,respectively.The kinetics curves of recrystallization for twin-roll casting AZ31 magnesium alloy were obtained.