摘要
A1GaN/GaN high electron mobility transistors （HEMTs） were exposed to 1 MeV neutron irradiation at a neutron ftuence of 1 × 10^15 cm-2. The dc characteristics of the devices, such as the drain saturation current and the maximum transconductance, decreased after neutron irradiation. The gate leakage currents increased obviously after neutron irradiation. However, the rf characteristics, such as the cut-off frequency and the maximum frequency, were hardly affected by neutron irradiation. The A1GaN/GaN heterojunctions have been employed for the better understanding of the degradation mechanism. It is shown in the Hall measurements and capacitance voltage tests that the mobility and concentration of two-dimensional electron gas （2DEG） decreased after neutron irradiation. Tbere was no evidence of the full-width at half-maximum of X-ray diffraction （XRD） rocking curve changing after irradiation, so the dislocation was not influenced by neutron irradiation. It is concluded that the point defects induced in A1GaN and GaN by neutron irradiation are the dominant mechanisms responsible for performance degradations of A1GaN/GaN HEMT devices.
A1GaN/GaN high electron mobility transistors （HEMTs） were exposed to 1 MeV neutron irradiation at a neutron ftuence of 1 × 10^15 cm-2. The dc characteristics of the devices, such as the drain saturation current and the maximum transconductance, decreased after neutron irradiation. The gate leakage currents increased obviously after neutron irradiation. However, the rf characteristics, such as the cut-off frequency and the maximum frequency, were hardly affected by neutron irradiation. The A1GaN/GaN heterojunctions have been employed for the better understanding of the degradation mechanism. It is shown in the Hall measurements and capacitance voltage tests that the mobility and concentration of two-dimensional electron gas （2DEG） decreased after neutron irradiation. Tbere was no evidence of the full-width at half-maximum of X-ray diffraction （XRD） rocking curve changing after irradiation, so the dislocation was not influenced by neutron irradiation. It is concluded that the point defects induced in A1GaN and GaN by neutron irradiation are the dominant mechanisms responsible for performance degradations of A1GaN/GaN HEMT devices.
基金
Project supported by the Major Program and Key Program of National Natural Science Foundation of China (Grant Nos. 60890191 and 60736033)