摘要
以直流电弧等离子体法自制的超细银粉为原料,固定浆料配比及制备工艺,通过改变浆料烧成工艺制度,结合扫描电子显微镜(SEM)、差热分析(DSC)等分析手段,系统研究了烧成峰值温度和保温时间对最终烧成厚膜导体性能的影响。结果表明,随着烧成峰值温度升高,保温时间延长,导体膜层方阻先减小,后增大;可焊性、耐焊性也具有先变好后变差的趋势。推荐较好的烧成工艺制度为:烧成峰值温度为850℃,保温20 min。
The silver thick film conductor self - designed DC arc plasma evaporation paste was made with the ultrafine silver powders prepared by device. The influences of peak firing temperature and sintering holding time on the properties of the thick film were studied systematically. The SEM and DSC were em- ployed to observe the surface morphology and to determine the firing schedule. The results show that, with the increase of peak firing temperature and sintering holding time, the sheet resistivity of the conductor is first decreased and then increased, the weldability, soldering resistance are good first and then trending deterioration. The preferable paste sintering technology is recommended that peak firing temperature is 850℃ and sintering holding time is 20 min.
出处
《贵金属》
CAS
CSCD
北大核心
2012年第1期5-9,共5页
Precious Metals
基金
国家自然科学基金项目(10502025)
江苏省社会发展项目(BS2007120)资助
关键词
金属材料
超细银粉
厚膜导体浆料
烧成工艺
性能
metal material
ultrafine silver powders
thick film conductor paste
sintering technology
properties