分析了该钢中铁素体形成的原因,介绍了如何控制其铁素体的含量,提出了控制该钢中铁素体含量的具体方法,基本解决了1Cr13叶片型不锈钢的δ-铁素体不合的问题。
The forming reasons of ferrite in this steel had been analyzed. This article introduced how to control the ferrite content in the steel and gave the concrete method to control the ferrite content in this steel. The problem of unsatisfactory δ- ferrite content of 1Cr 13 for turbine blade has been basically solved.