利用配有BM分离型螺杆的单螺杆挤出机研究了聚碳酸酯(PC)颗粒在不同条件下经熔融挤出后的特性黏数([η])和熔体流动速率(MFR)的变化。结果发现:在300℃以下的挤出温度、不同螺杆转速下对烘干的PC树脂挤出加工时,基本不会改变PC的[η]和MFR,因而难以用测定[η]或相对分子质量的方法判别PC是新料还是回收料;在120℃,-0.1 MPa干燥l.0 h可保证把料彻底烘干,延长干燥时间可促进PC料的固相缩聚,提高[η],有利于PC的加工;经多次热加工的PC树脂或PC含有少量水分时,挤出产物的[η]明显下降,MFR显著变大,不利于加工。
The variation in intrinsic viscosity ([η]) and meh flow rate (MFR) of polycarbonate (PC) particles after melt extrusion under different conditions was studied by means of a single-screw extruder equipped with a BM separable type screw. The experimental results show that the [η] and MFR have little change when the dried PC is extruded at different speeds of the extruder screw below 300 ℃. Therefore, it is rather difficult to judge whether the PC particles are fresh or recycled material merely according to the test of [η] or relative molecular mass. The PC material can be dried completely after being treated in a vacuum oven for an hour at 120 ℃ under -0.1 MPa. Lengthening drying time can not only facilitate the PC's solid phase polycondensation, but also raise its [η] and further benefit its processability. The PC extrudate's [η] decreases obviously while its MFR increases noticeably in case the PC resin undergoes multiple thermal treatments or contains a small amount of water, which militates against the processing of the PC material.
出处
《合成树脂及塑料》
CAS
北大核心
2012年第2期59-62,共4页
China Synthetic Resin and Plastics
关键词
聚碳酸酯
挤出
特性黏数
单螺杆挤出机
polycarbonate
extrusion
intrinsic viscosity
single-screw extruder