螺旋肋钢丝在拉拔过程中有005～015mm的缩径。经分析有的缩径由工艺缺陷导致;有的则是人为造成的。应严加控制以防止成材率下降和力学性能降低。
In the drawing process there were 0 05～0 15?mm diameter shrinking phenomena happened in the products which were caused by either process defects or man made defects and will decrease the useful product rate and lower the physical properties if not well controlled