摘要
The superplastic deformation diffusion bonding of 00Cr25Ni7Mo3N duplex stainless steel was performed on a hot simulator. The microstructure of the bonding interface was characterized by scanning electron microscopy （SEM） and electron backscatter diffraction （EBSD）. The mechanical properties of the specimen were investigated by a shear strength test. The results indicated that the shear strength was improved with the increase of superplastic deformation reduction. When the deformation reduction was up to 50%, the shear strength of the specimen achieved 417 Mpa, approaching to that of the base metal. In addtion, the superplastic diffusion bonding technique was not very sensitive to surface roughness levels. When the surface roughness of the bonding specimen surpassed 0.416 pan （level G2）, the shear strength achieved at least 381 MPa.
The superplastic deformation diffusion bonding of 00Cr25Ni7Mo3N duplex stainless steel was performed on a hot simulator. The microstructure of the bonding interface was characterized by scanning electron microscopy （SEM） and electron backscatter diffraction （EBSD）. The mechanical properties of the specimen were investigated by a shear strength test. The results indicated that the shear strength was improved with the increase of superplastic deformation reduction. When the deformation reduction was up to 50%, the shear strength of the specimen achieved 417 Mpa, approaching to that of the base metal. In addtion, the superplastic diffusion bonding technique was not very sensitive to surface roughness levels. When the surface roughness of the bonding specimen surpassed 0.416 pan （level G2）, the shear strength achieved at least 381 MPa.