摘要
Macro-mesoporous γ-alumina support（MMA） was prepared by a sol-gel route in aqueous medium using pseudo-boehmite as aluminum source and polystyrene microspheres and Pluronic P123 as hard and soft dual templates,respectively.MMA had a BET specific surface area of about 259 m2 g-1,total pore volume of about 1.61 cm3 g-1,macropore diameter of about 102 nm,and mesopore diameter of about 14 nm.Re2O7/MMA and conventional Re2O7/Al2O3 were prepared by a incipient-wetness impregnation method,and their catalytic performances in the metathesis of 1-butene and 2-butene were tested in a fixed-bed tubular reactor.The result showed that Re2O7/MMA possessed higher activity and far longer working life-span than conventional Re2O7/Al2O3.
Macro-mesoporous γ-alumina support（MMA） was prepared by a sol-gel route in aqueous medium using pseudo-boehmite as aluminum source and polystyrene microspheres and Pluronic P123 as hard and soft dual templates,respectively.MMA had a BET specific surface area of about 259 m2 g-1,total pore volume of about 1.61 cm3 g-1,macropore diameter of about 102 nm,and mesopore diameter of about 14 nm.Re2O7/MMA and conventional Re2O7/Al2O3 were prepared by a incipient-wetness impregnation method,and their catalytic performances in the metathesis of 1-butene and 2-butene were tested in a fixed-bed tubular reactor.The result showed that Re2O7/MMA possessed higher activity and far longer working life-span than conventional Re2O7/Al2O3.
基金
supported by the National Natural Science Foundation of China (Grant No:20976192)
SINOPEC Jiujiang Petrochemical Company (G2810-09-ZS-0027)