摘要
Nanocrystalline calcium aluminates with different CaO/Al2O3 ratios were prepared by a facile co-precipitation method using Poly（ethylene glycol）-block-poly（propylene glycol）-block-poly（ethylene glycol） （PEG-PPG-PEG, MW： 5800） as a surfactant. They were employed as catalyst support for nickel catalysts in methane reforming with carbon dioxide. The prepared samples were characterized by X-ray diffraction （XRD）, N2 adsorption （BET）, temperature-programmed reduction and oxidation （TPR-TPO）, and scanning electron microscopy （SEM） techniques. Catalysts showed a relatively high catalytic activity and stability. TPR analysis revealed that the catalysts with higher CaO content are more difficult to be reduced. TPO analysis showed that the 5 wt%Ni/CA and 5 wt%Ni/C12A7 catalysts with higher CaO amount were effective against coke deposition.
Nanocrystalline calcium aluminates with different CaO/Al2O3 ratios were prepared by a facile co-precipitation method using Poly（ethylene glycol）-block-poly（propylene glycol）-block-poly（ethylene glycol） （PEG-PPG-PEG, MW： 5800） as a surfactant. They were employed as catalyst support for nickel catalysts in methane reforming with carbon dioxide. The prepared samples were characterized by X-ray diffraction （XRD）, N2 adsorption （BET）, temperature-programmed reduction and oxidation （TPR-TPO）, and scanning electron microscopy （SEM） techniques. Catalysts showed a relatively high catalytic activity and stability. TPR analysis revealed that the catalysts with higher CaO content are more difficult to be reduced. TPO analysis showed that the 5 wt%Ni/CA and 5 wt%Ni/C12A7 catalysts with higher CaO amount were effective against coke deposition.