In order to precisely control the final temperature of molten steel in RH （Ruhrstahl Heraeus）-TOP blowing refining, the final temperature prediction models of molten steel in RH-TOP blowing refining process for Interstitial Free （IF） steel production were established under the condition of oxygen blowing and non-oxygen blowing respec- tively. The results show that the beginning molten steel temperature of refining and the amount of added scrap were influential factors, the baking temperature in vacuum chamber was a factor that had small influence. When the model was operated, the hitting probability was above 95%（under the condition of both oxygen blowing and non-oxygen blo- wing） of prediction deviation ±10℃. The accuracy is analyzed.
In order to precisely control the final temperature of molten steel in RH （Ruhrstahl Heraeus）-TOP blowing refining, the final temperature prediction models of molten steel in RH-TOP blowing refining process for Interstitial Free （IF） steel production were established under the condition of oxygen blowing and non-oxygen blowing respec- tively. The results show that the beginning molten steel temperature of refining and the amount of added scrap were influential factors, the baking temperature in vacuum chamber was a factor that had small influence. When the model was operated, the hitting probability was above 95%（under the condition of both oxygen blowing and non-oxygen blo- wing） of prediction deviation ±10℃. The accuracy is analyzed.
作者
WANG Yu-nan1, BAO Yan-ping1, CUI Heng2, CHEN Bin3, JI Chen-xi3 (1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China
2. Engineering Research Institute, University of Science and Technology Beijing, Beijing 100083, China
3. Shougang Research Institute of Technology, Beijing 100041, China)
基金
Sponsored by National Key Technology Research and Development Program in 11th Five-Year Plan of China(2006BAE03A06)