给水泵轴断裂失效分析 被引量:7

Fracture Analysis of the Water Pump Shaft
下载PDF
导出
摘要 以某电厂给水泵轴运行仅8个月即发生断裂为例,对泵轴进行化学成分、力学性能、金相组织、断口宏观和扫描电镜分析等试验分析,阐述了泵轴的断裂原因是叶轮与泵轴之间配合间隙过大,使泵轴键槽处周向应力增大,在键槽底部边缘形成了多个疲劳源,先周向疲劳扩展产生鳞剥,后由径向旋转弯曲及扭转疲劳扩展至断裂。 A water pump shaft broke after it had been under service for only 8 months.According to a series of test analysis such as chemical constituents,mechanical properties,metallographic structure,macrofractography and scanning electron microscopy,it was concluded that the fracture was caused by large clearance between impeller and pump shaft,so that the circumferential stress at key slot increased and fatigue source formed.Primarily,circle fatigue developed into chipping,and then developed into radial rotating and bending before fracture finally occurred.
出处 《山西电力》 2012年第2期42-44,共3页 Shanxi Electric Power
关键词 泵轴 疲劳断裂 应力 pump shaft fatigue fracture stress
  • 相关文献

参考文献4

  • 1姜求志,王金瑞.火力发电厂金属材料手册[M].北京:中国电力出版社,2009:793-802.
  • 2钟群鹏.断口学[M].北京:高等教育出版社,2005.
  • 3C.亨利,D.豪斯特曼.宏观断口学及显微断口学[M].曾祥华译.北京:机械工业出版社,1979:58-90.
  • 4韩荣东,龚桂仙.40Cr钢端轴断裂分析[J].物理测试,2008,26(5):40-42. 被引量:9

二级参考文献2

共引文献41

同被引文献56

引证文献7

二级引证文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部