电流密度对摩擦喷射电沉积制备镍沉积层微观形貌及性能的影响 被引量:4

Effects of Current Density on Micromorphology and Property of Nickel Deposition Layer Prepared by Friction Jet Electrodeposition
下载PDF
导出
摘要 采用摩擦喷射电沉积系统制备了镍沉积层,用形貌仪、X射线衍射仪和显微硬度计等研究了镍沉积层的表面形貌、组织结构、晶粒平均尺寸和显微硬度随电流密度的变化。结果表明:硬质粒子能有效去除镍沉积层表面的吸附气泡和积瘤,获得表面较为平整光亮的沉积层;随着电流密度的增大,(111)、(200)和(220)晶面的择优取向度趋于一致,镍沉积层的表面粗糙度和晶粒平均尺寸先减小后增大,电流密度为80A.dm-2时表面粗糙度最小,电流密度为100A.dm-2时晶粒的平均尺寸最小,为9.67nm;显微硬度先增大后减小,当电流密度为80A.dm-2时最大。 The nickel deposition layer was prepared by friction jet electrodeposition system,the variation of the surface micromorphology,microstructure,average size of grain and microhardness of the nickel deposition layer as a function of current density was studied by micromorphology analysing,X-ray diffraction,microhardness testing and so on.The results show that the hard particles could effectively remove the hydrogen bubbles and nodules absorbed on nickel deposition layer surface,and obtain regular and smooth deposition layer.With the increase of the current density,the orientation degree of the lattice planes of(111),(200) and(220) converged,the surface roughness and average size of grains first decreased and then increased,the surface roughness was minimal when the current density was 80 A·dm-2,and the average size of grains,which was 9.67 nm,was minimal when the current density was 100 A·dm-2.The microhardness first increased and then decreased and it was maximal when the current density was 80 A·dm-2.
出处 《机械工程材料》 CAS CSCD 北大核心 2012年第4期17-20,29,共5页 Materials For Mechanical Engineering
基金 国家自然科学基金资助项目(50575104) 江苏省自然科学基金资助项目(BK2009375)
关键词 摩擦喷射电沉积 硬质粒子 电流密度 friction jet electrodeposition hard particle current density
  • 相关文献

参考文献11

二级参考文献89

共引文献108

同被引文献22

引证文献4

二级引证文献10

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部