High speed impact experiments of rectangular plate-shaped Zr 41 Ti 14 Cu 12.5 Ni 10 Be 22.5 bulk metallic glass（BMG） were performed using a two-stage light gas gun.Under spherical shock waves with impact velocities ranging from 0.503 km/s to 4.917 km/s,obvious traces of laminated spallation at the back（free） surface and melting（liquid droplets） at the impact point were observed.The angles about 0掳,17掳,36掳,and 90掳to the shocking direction were shown in the internal samples because of the interaction between the compressive shock waves and the rarefaction waves.The compressive normal stress was found to induce the consequent temperature rise in the core of the shear band.
High speed impact experiments of rectangular plate-shaped Zr 41 Ti 14 Cu 12.5 Ni 10 Be 22.5 bulk metallic glass（BMG） were performed using a two-stage light gas gun.Under spherical shock waves with impact velocities ranging from 0.503 km/s to 4.917 km/s,obvious traces of laminated spallation at the back（free） surface and melting（liquid droplets） at the impact point were observed.The angles about 0掳,17掳,36掳,and 90掳to the shocking direction were shown in the internal samples because of the interaction between the compressive shock waves and the rarefaction waves.The compressive normal stress was found to induce the consequent temperature rise in the core of the shear band.
基金
Project supported by the National Basic Research Program of China (Grant No. 2010CB731600)