分子量多分散性对AB二嵌段共聚物相行为的影响

Polydispersity Effect on Phase Behavior of Diblock Copolymer
下载PDF
导出
摘要 采用Monte Carlo方法研究了分子量多分散性对AB型嵌段共聚物相行为的影响.通过调整嵌段共聚物中组分含量,考察了整体多分散性和单嵌段多分散性对嵌段共聚物共混物的有序-无序转变(Order-disordertransition,ODT)、形貌及链尺寸的影响.研究结果表明,多分散度的增大使无序相向较大χN区域略微移动,形成的片层结构厚度增加.在形成微观有序形貌后,较大分散度时各亚组分的链会得到更大的伸展,表明分子链堆积受挫的程度减小,因此,涨落作用受到的抑制作用减小,无序相区向更低温度区域移动. Effect of polydispersity on phase behavior of diblock copolymer was studied by Monte Carlo simulation.In order to evaluate the polydispersity effect,block copolymer blends including three different components were utilized as models in the simulation.By controlling the weight fractions of the component in copolymer blend,the influence of two different types of polydispersity effects(i.e.overall polydispersity effect and single block polydispersity effect,respectively) on order-disorder transition(ODT),conformations,and chain size of polymers were investigated.The results show that the increasing of index of polydispersity(PDI) can cause the ODT temperature slightly shifts to a lower temperature region.And it can also induce the increasing of the spacing thickness of the newly formed lamellar structure.Based on microscopic conformation analysis,polymer chains tend to stretch more at larger PDIs,which reveals the decreasing of accumulation degree of polymer chains.Therefore,the inhibition effect on fluctuation diminishes and the disordered phase shifts to the lower temperature region.
出处 《高等学校化学学报》 SCIE EI CAS CSCD 北大核心 2012年第5期1116-1120,共5页 Chemical Journal of Chinese Universities
基金 国家自然科学基金(批准号:91123029 61077066 50902128)资助
关键词 MONTECARLO模拟 分子量多分散性 AB二嵌段共聚物 相行为 Monte Carlo simulation Polydispersity effect Diblock copolymer Phase behavior
  • 引文网络
  • 相关文献

参考文献11

  • 1HANXiangGang(韩向刚) ZHANGChengXiang(张程祥).高等学校化学学报,2010,31(3):1575-1578.
  • 2Milner S. , Witten T. , Cates M.. Macromolecules[J]. 1989, 22:853-861.
  • 3陈梨俊,张志杰,吕中元,孙家锺.聚合物链长及表面吸附强度对三维受限下嵌段共聚物微观相分离的影响[J].高等学校化学学报,2007,28(2):316-319. 被引量:2
  • 4Burger C. , Ruland W. , Semenov A.. Macromolecules [ J], 1990, 23 : 3339-3346.
  • 5Thompson R. , Matsen M.. Phys. Rev. Lett. [J]. 2000, 85:670-673.
  • 6Fredrickson G.. The Equilibrium Theory of Inhomogeneous Polymers [ M ], Oxford : Clarendon Press, 2006.
  • 7Sides S. , Fredrickson G.. J. Chem. Phys. [J]. 2004, 121:4974-4986.
  • 8Lynd N. , Hillmyer M.. Macromolecules[ J] , 2005, 38 : 8803-8810.
  • 9Li Y. , Huang Q. , Shi T. , An L.. J. Phys. Chem. B[J]. 2006, 110:23502-23506.
  • 10Matsen M. W.. Phys. Rev. Lett. [J]. 2007, 99:148304-1-148304-4.

二级参考文献17

  • 1叶祥贵,孙昭艳,安立佳.利用TDGL方法模拟嵌段共聚物链长和浓度对A/B/A-B三组分体系相形态演化的影响[J].高等学校化学学报,2005,26(2):356-361. 被引量:2
  • 2Bucknall D. G. , Anderson H. L.. Science[J], 2003, 302:1904-1905.
  • 3Matsen M. W. , Schick M.. Phys. Rev. Lett. [J], 1994, 72:2660-2663.
  • 4Fasolka M. J., Mayes A. M.. Annu. Rev. Mater. Res. [J], 2001,31:323-355.
  • 5Kim S. O. , Solak H. H. , Stoykovich M. P. , et al.. Nature[J], 2003, 424:411-414.
  • 6Silva A. S. , Mitchell C. A. , Tse M. F. , et al.. J. Chem. Phys. [J], 2001, 115:7166-7174.
  • 7Li H. W. , Huck W. T. S.. Nano Lett. [J], 2004, 4:1633-1636.
  • 8Shin K. , Xiang H. , Moon S. , et al.. Science[J], 2004, 306:76.
  • 9Arsenault A. C., Rider D. A., Tetreault N., et al.. J. Am. Chem. Soc. [J], 2005, 127:9954-9955.
  • 10Zvelindovsky A. V. , Sevink G. J. A. , van Vlimmeren B. A. C. , et al.. Phys. Rev. E[J], 1998, 57:R4879-R4882.

共引文献1

;
使用帮助 返回顶部