三次热循环对2.25Cr1Mo钢组织的影响

Effect of Ternary Thermal Cycle on Microstructure of 2.25Cr1Mo Steel

通过扫描电镜(SEM)、能谱(EDS)分析方法,对2.25Cr1Mo钢经受三次热循环后的组织进行了分析。结果表明,经过三次热循环作用,获得贝氏体组织。经三次热循环—三次热循环中最高峰值温度1 195℃,三次热循环总的t8/5达97s以上的作用时,晶粒尺寸并未发生明显长大。由于第一次热循环冷却过程中没有发生相变,没能产生第二次热循环峰值温度的晶粒细化作用使晶粒尺寸细化。试样热循环作用后,对试样的能谱分析结果表明,析出相微区成分相近,以Fe元素为主要成分,可推测形成了Fe,Cr,Mo碳化物析出相。

The effect of ternary thermal cycle on microstructure of 2.25Cr1Mo steel was analyzed by SEM and EDS.The results show that ternary thermal cycle results in the formation of bainite.Grain size does not grow larger obviously after subjected ternary thermal cycle of maximum peak temperature 1 195 ℃,total t8/5 more than 97 s of ternary thermal cycle.Because phase transformation does not occur upon cooling of first thermal cycle,effect of peak temperature of second thermal cycle on grain size,which may result in grain finer does happen.EDS analyses of specimen after thermal cycle indicate that micro zone compositions of precipitated phase are similar and Fe element in the majority.It is assumed that precipitated phases formed are Fe,Cr,Mo carbides.