Oxidation and Thermal Shock Behavior of a Glass-Alumina Composite Coating on K38G Superalloy at 1000℃
被引量:4
Oxidation and Thermal Shock Behavior of a Glass-Alumina Composite Coating on K38G Superalloy at 1000℃
基金
supported by the Knowledg Innovation Program of the Chinese Academy of Sciences Grant No. YYYJ-0912
the National Natural Scienc Foundation of China,Grant No. 50774074
参考文献23
-
1G.W. Goward: Surf. Coat. Technol., 1998, 108, 73.
-
2R. Sivakumar and B.L. Mordike: Surf. Coat. Tech- nol., 1989, 37, 136.
-
3V. Teixeira: Vacuum, 2002, 64, 393.
-
4W.D. Kingery: J. Am. Ceram." Soc., 1955, 38, 3.
-
5M. Matsubara and S. Hanada: J. Jpn. Inst. Met., 1999, 63, 112.
-
6I.W.Donald: J. Mater. Sci., 1993, 28, 2841.
-
7A. Pazo, E. Saiz and A.P. Tomsia: Acta Mater., 1998, 46, 2551.
-
8I.W. Donald, B.L. Metcalfe and L.A. Gerrard: J. Am. Ceram. Soc., 2008, 91,715.
-
9S. Das, S. Datta, D. Basu and G.C. Das: Ceram. Int., 2008, 34, 1215.
-
10M.H. Chen, S.L. Zhu, M.L. Shen, F.H. Wang and Y. Niu: Mater. Sci. Eng. A, 2011~ 528, 1360.
同被引文献59
-
1李护林,王国强.液体火箭发动机涡轮燃气通道用搪瓷涂层性能改善研究[J].航天制造技术,2013(3):1-4. 被引量:3
-
2米丰毅,朱圣龙.搪瓷涂层700℃长期抗高温氧化和热腐蚀行为研究[J].腐蚀科学与防护技术,2015,27(3):254-258. 被引量:9
-
3陈琳,张三平,周学杰.降低热喷涂涂层孔隙率的工艺技术[J].上海金属,2004,26(4):41-43. 被引量:12
-
4黄智勇,李昌奂.纳米复合搪瓷涂层在液体火箭发动机的应用研究[J].火箭推进,2005,31(2):44-50. 被引量:2
-
5朱立群,张楚豫,李卫平.非晶态Ni-W合金镀层的高温氧化性能研究[J].材料工程,1996(4):14-16. 被引量:7
-
6倪亚茹,陆春华,张焱,张其土,许仲梓.稀土对硼铝硅酸盐玻璃形成及热膨胀性能的影响[J].稀土,2006,27(1):83-86. 被引量:5
-
7Yugeswaran S, Kobayashi A, Suresh K, et al. Characte- rization of gas tunnel type plasma sprayed TiN reinforced Fe-based metallic glass coatings[J]. J Alloys Compd,2013, 551(25) :168.
-
8Gargarella P, Almeida A, Vilar R, et al. Formation of Fe- based glassy matrix composite coatings by laser processing [J]. Surf Coat Techn, 2014,240 (15) : 336.
-
9Zheng Z B, Zheng Y G, Sun W H, et al. Effect of applied potential on passivation and erosion-corrosion of a Fe-based amorphous metallic coating under slurry impingement[J]. Corros Sei,2014,82 : 115.
-
10Zhang C, Liu L, Chan K C, et al. Wear behavior of HVOF- sprayed Fe-based amorphous coatings[J]. Intermetallics, 2012,29 : 80.
引证文献4
-
1郭策安,陈明辉,廖依敏,苏北,谢冬柏,朱圣龙,王福会.模拟燃气热冲击条件下搪瓷基复合涂层的防护机理研究[J].金属学报,2018,54(12):1825-1832. 被引量:3
-
2罗大为,李聪勃,陈为为.非晶态合金涂层的研究进展[J].材料导报,2015,29(5):88-94. 被引量:2
-
3薛洪喜,崔永凤,徐坤山,刘杰,李志恒.搪玻璃使用寿命及其理化性能研究进展[J].硅酸盐通报,2020,39(12):3991-3997. 被引量:4
-
4杜撰,陈林,孟国辉,朱昌发,赵鼎,王国强.搪瓷涂层改性技术及应用研究进展[J].材料保护,2023,56(4):158-168. 被引量:1
二级引证文献10
-
1范建文,梁秀兵,张志彬,陈永雄,商俊超.AlNiZr基非晶纳米晶复合涂层组织与性能研究[J].装甲兵工程学院学报,2017,31(3):94-99. 被引量:1
-
2梁秀兵,范建文,张志彬,陈永雄.铝基非晶纳米晶复合涂层显微组织与腐蚀性能研究[J].金属学报,2018,54(8):1193-1203. 被引量:11
-
3廖依敏,陈明辉,王福会,朱圣龙.自修复金属搪瓷高温防护涂层[J].表面技术,2020,49(1):25-34. 被引量:6
-
4郑杰希,宫奎源,张红阳,薛洪喜,徐坤山,刘杰.助熔剂和密着剂对搪玻璃的作用机理及其研究进展[J].硅酸盐通报,2022,41(8):2918-2926. 被引量:1
-
5孙全社,徐春,魏娇,王双成.搪玻璃用热轧中厚钢板氢穿透时间及贮氢性能[J].钢铁,2022,57(12):161-168. 被引量:3
-
6杜撰,陈林,孟国辉,朱昌发,赵鼎,王国强.搪瓷涂层改性技术及应用研究进展[J].材料保护,2023,56(4):158-168. 被引量:1
-
7李响.搪玻璃反应釜现场局部快速修补技术应用概述[J].化工装备技术,2023,44(2):1-3.
-
8杨均,姚青,李怀峰,卞清,裴妍娜,薛召露.等离子喷涂硅酸盐搪瓷涂层及其热循环行为研究[J].电镀与涂饰,2024,43(2):76-83.
-
9王超,郑龙席,王渤文,程悦,张军利,李勍.结构参数对闭口体系新型激波吹灰器工作特性的影响研究[J].西北工业大学学报,2024,42(2):269-277.
-
10徐子强,张建军,钟锦林,郭玉,王杰,张梅,李泰来,孙雅宁,徐坤山.氧化锆的含量和颗粒尺寸对搪玻璃弯曲性能的影响[J].玻璃搪瓷与眼镜,2024,52(6):1-6.
-
1赵凤林,李仁超,许诚信,王林英,赵进喜,崔润琴,李秀文.氧化铝夹杂的形态[J].钢铁,1990,25(2):18-22. 被引量:4
-
2王福会,朱圣龙,楼翰一,吴维(山文).Al_2O_3涂层对高温合金K38G热腐蚀的影响[J].腐蚀科学与防护技术,1993,5(1):32-37. 被引量:1
-
3仵永刚,魏建文.4053160Y滚子外径面产生磁痕的原因分析[J].轴承技术,2009(2):29-31. 被引量:1
-
4仵永刚,盛伟,魏建文.4053160Y滚子柱面产生磁痕的原因分析[J].轴承,2008(7):35-36. 被引量:4
-
5刘靖,姚晓乐,贺景春.稀土La和Ce对25CrMoVB钢夹杂物的影响[J].金属热处理,2012,37(10):17-20. 被引量:7
-
6卢凤喜,王向成.减少冷轧钢板线状和白筋缺陷的措施[J].轧钢,2006,23(6):45-47. 被引量:3
-
7易艳良,梁益龙,王攀智,杨明.CL60车轮钢热处理后的接触疲劳寿命[J].金属热处理,2014,39(3):41-45. 被引量:5
-
8小方坯连铸过程中水口堵塞的动力学模型[J].世界钢铁,2011,11(2):71-71.
-
9张敏,陈阳阳,刘明志,李继红.超低碳贝氏体钢埋弧焊焊接接头韧化机理分析[J].焊接学报,2016,37(6):45-49. 被引量:10
-
10张含卓,方亮,周亚国,石高亮.化学镀纳米晶铜层的显微组织与腐蚀特性[J].稀有金属材料与工程,2012,41(S2):239-242.