摘要
Effects of different silicon carbide contents on thermal shock resistance properties of mullite-bauxite castable refractory were analyzed respectively by taking the mullite,bauxite as main raw materials and taking calcium aluminate cement as a binding system.After 24 h curing in mould and another 24 h curing at 110℃ after demoulding,the samples were heated at 1000,1300 and 1500℃for 3 h in air,respectively.The bulk density,thermal expansion coefficient and thermal shock resistance were examined.The results showed that there was a great effect of content of SiC on bulk density,thermal expansion coefficient and thermal shock resistance of mullite-bauxite castable.Under the experimental conditions,the castable performed the best thermal shock resistance when w(SiC)=5%-10%.
Effects of different silicon carbide contents on thermal shock resistance properties of mullite-bauxite castable refractory were analyzed respectively by taking the mullite,bauxite as main raw materials and taking calcium aluminate cement as a binding system.After 24 h curing in mould and another 24 h curing at 110℃ after demoulding,the samples were heated at 1000,1300 and 1500℃for 3 h in air,respectively.The bulk density,thermal expansion coefficient and thermal shock resistance were examined.The results showed that there was a great effect of content of SiC on bulk density,thermal expansion coefficient and thermal shock resistance of mullite-bauxite castable.Under the experimental conditions,the castable performed the best thermal shock resistance when w（SiC）=5%-10%.