A method of direct contact membrane distillation （DCMD） with a self-made hollow polyvinylidene fluoride membrane was applied to prepare high concentration polyaluminum chloride （PACl） with high Alb content based on chemical synthesis. The permeate flux and Al species distribution were investigated. The experimental results showed that the permeate flux decreased from 14 to 6 kg/（m2·hr） at the end of the DCMD process, which can be mainly attributed to the formation of NaCl deposits on the membrane surface. The Alb content decreased slightly, only from 86.3% to 84.4%, when the DCMD experiment finished, correspondingly the Alc content increased slightly from 7.2% to 8.5%, and the Ala content remained at 7% during the whole DCMD process. A PACl with Alb content of 84% at total aluminum concentration 2.2 mol/L was successfully prepared by the chemical synthesis-DCMD method.
A method of direct contact membrane distillation （DCMD） with a self-made hollow polyvinylidene fluoride membrane was applied to prepare high concentration polyaluminum chloride （PACl） with high Alb content based on chemical synthesis. The permeate flux and Al species distribution were investigated. The experimental results showed that the permeate flux decreased from 14 to 6 kg/（m2·hr） at the end of the DCMD process, which can be mainly attributed to the formation of NaCl deposits on the membrane surface. The Alb content decreased slightly, only from 86.3% to 84.4%, when the DCMD experiment finished, correspondingly the Alc content increased slightly from 7.2% to 8.5%, and the Ala content remained at 7% during the whole DCMD process. A PACl with Alb content of 84% at total aluminum concentration 2.2 mol/L was successfully prepared by the chemical synthesis-DCMD method.
基金
supported by the National High Technology Research and Development Program (863) of China (No.2007AA06Z339, 2009AA062901, 2008AA06A414)
the National Natural Science Foundation of China (No.50978245, 21076219)