摘要
Magnesia chrome bricks were prepared with fiLsed MgO- Cr2 O3 synthesized material, fused magnesite and ：hrome ore as main starting materials. Nano-Al2O3 was tdded into refractories （ 2% , 4% and 6% in mass ） ;ubstit,ting for Al203 micropowder. After m＆ing and ;haping, the bricks were fired at 1 550 ℃, 1 600 91℃, t 650 ℃ and 1 750℃, respectively. The microstruc-ure , sintering property, mechanical properties, thermal ;kock resistance and shtg resistance of the specimens with he addition of nano-Al2O3 were investigated. The results indicate that the performance of brick with 4 mass% of nano-Al2O3 is greatly improred afier firing at 1 650 ℃.
Magnesia chrome bricks were prepared with fiLsed MgO- Cr2 O3 synthesized material, fused magnesite and ：hrome ore as main starting materials. Nano-Al2O3 was tdded into refractories （ 2% , 4% and 6% in mass ） ;ubstit,ting for Al203 micropowder. After m＆ing and ;haping, the bricks were fired at 1 550 ℃, 1 600 91℃, t 650 ℃ and 1 750℃, respectively. The microstruc-ure , sintering property, mechanical properties, thermal ;kock resistance and shtg resistance of the specimens with he addition of nano-Al2O3 were investigated. The results indicate that the performance of brick with 4 mass% of nano-Al2O3 is greatly improred afier firing at 1 650 ℃.