摘要
Yb x Co 4 Sb 12 polycrystals were fabricated by vacuum melting combined with hot-press sintering.The effect of Yb-filling on thermoelectric property of unfilled skutterudite CoSb 3 was investigated,which indicated the enhancement of the power factor of the material.Transport properties of materials changed from semi-conductor to semi-metal during the measurement of electrical conductivity,which indicated the change of electronic band structure.The maximum value of electrical conductivity was about 190000 S/m at 300 K for all samples.On the basis of Yb-filling,power factor of Yb 0.2 Co 4 Sb 12 reached 5-6 mW/（m·K） during the measurement temperature.Thermal conductivity decreased with increase of Yb content,and the thermal conductivity of Yb 0.2 Co 4 Sb 12 reached 3.2 W/（m·K） at 600 K.The ZT value of Yb 0.2 Co 4 Sb 12 reached 1.16 at 700 K due to positive contribution from high power factor and low thermal conductivity.
Yb x Co 4 Sb 12 polycrystals were fabricated by vacuum melting combined with hot-press sintering.The effect of Yb-filling on thermoelectric property of unfilled skutterudite CoSb 3 was investigated,which indicated the enhancement of the power factor of the material.Transport properties of materials changed from semi-conductor to semi-metal during the measurement of electrical conductivity,which indicated the change of electronic band structure.The maximum value of electrical conductivity was about 190000 S/m at 300 K for all samples.On the basis of Yb-filling,power factor of Yb 0.2 Co 4 Sb 12 reached 5-6 mW/（m·K） during the measurement temperature.Thermal conductivity decreased with increase of Yb content,and the thermal conductivity of Yb 0.2 Co 4 Sb 12 reached 3.2 W/（m·K） at 600 K.The ZT value of Yb 0.2 Co 4 Sb 12 reached 1.16 at 700 K due to positive contribution from high power factor and low thermal conductivity.
基金
supported by National Natural Science Foundation of China (50801054)
the Research Award Fund for Outstanding Young Scientist in Shandong Province,China (BS2011CL031)