The as-sintered sinter skin and the polished section of WC-11Co-0.4Cr 3 C 2-0.3VC-0.2RE（RE=mischmetal with La/Ce ratio of 0.65） alloy were analyzed.It was shown that the microstructures on the skin and in the inner part of the alloy were all characterized with a WC＋β＋M structure,where β was a cobalt-based binder phase and M represented a RE-containing phase.There existed an inward diffusion of S atoms,which caught and fixed the Ce atoms in the alloy and an outward diffusion of La atoms during the sintering process.Consequently,the M phase was characterized with the decreased La/Ce ratio（0.59） in the inner part and the increased La/Ce ratio（1.01） on the skin.The M phase on the skin was characterized with a γ-Ce 2 S 3 type structure.To suppress the long range migration of rare earth to the skin,S in the sintering atmosphere had to be eliminated.
The as-sintered sinter skin and the polished section of WC-11Co-0.4Cr 3 C 2-0.3VC-0.2RE（RE=mischmetal with La/Ce ratio of 0.65） alloy were analyzed.It was shown that the microstructures on the skin and in the inner part of the alloy were all characterized with a WC＋β＋M structure,where β was a cobalt-based binder phase and M represented a RE-containing phase.There existed an inward diffusion of S atoms,which caught and fixed the Ce atoms in the alloy and an outward diffusion of La atoms during the sintering process.Consequently,the M phase was characterized with the decreased La/Ce ratio（0.59） in the inner part and the increased La/Ce ratio（1.01） on the skin.The M phase on the skin was characterized with a γ-Ce 2 S 3 type structure.To suppress the long range migration of rare earth to the skin,S in the sintering atmosphere had to be eliminated.
基金
supported by National Natural Science Foundation of China (51074189,50823006)
Science and Technology Planning Project Founda-tion of Hunan Province,China (2010FJ2006)
Research Foundation for the Doctoral Program of Higher Education of China (20100162110001)
the National Science & Technology Special Foundation of China (2011BAE09B02,2012ZX04003021)