摘要
研究了W含量为15%~30%的Ni-W合金的组织形貌、相结构以及显微硬度。结果表明:不同W含量的4种合金都形成了Ni(W)单相固溶体;随着W含量的增加,晶界处氧化物增加,合金显微硬度也随着增加。
The microstructure, phase composition and microhardness of the Ni-W alloys with W content of 15%-30% were studied. The results show that the phase composition of four kinds of alloys are single phase Ni(W) solid solution in the microstructure; with the increase of the content of W, the oxides of grain boundary increases, and the microhardness also increases.
出处
《铸造技术》
CAS
北大核心
2012年第6期688-690,共3页
Foundry Technology