Si phase morphology and mechanical properties of ZL107 Al alloy improved by La modification and heat treatment

La变质和热处理复合作用下ZL107铝合金中Si相形态演化及其力学性能(英文)

The phase morphology evolution during the solid solution treatment and then artificial aging of the La-modified ZL107 Al alloy was studied. The results show that when the solid solution was held at 560 ℃ for 6 h, only partial Si phase dissolved into the matrix; however, the precipitation also occurred during the artificial aging process. The precipitation process in Al-Si alloys with or without La-modification was compared. After modification and heat treatment, the mechanical properties of the alloy were greatly enhanced, due to the modification and uniform distribution of Si phase.

研究ZL107铝合金经过固溶和时效处理后的Si相形态演化及其对力学性能的影响。结果表明,当合金在560°C固溶处理6h后,有部分Si相固溶进入基体,但在随后的时效过程中Si相会重新析出。比较了变质和未变质ZL107合金的固溶时效过程。通过La变质处理再固溶时效,ZL107合金中的Si相形态明显细化,合金的力学性能提高幅度更大。