前驱液pH值对2ZnO·2.2B_2O_3·3H_2O∶Eu^(3+)荧光粉发光性能的影响 被引量:2

Effect of pH Value of Precursor Solution on the Luminescent Properties of 2ZnO·2.2B_2O_3·3H_2O∶Eu^(3+) Phosphor
下载PDF
导出
摘要 采用水热法,通过氨水调节前驱液的pH值,制备了一系列2ZnO.2.2B2O3.3H2O∶Eu3+样品。对所制备的样品进行X射线衍射和荧光光谱分析。研究结果表明:前驱液的pH值影响2ZnO.2.2B2O3.3H2O的结晶程度,在中性条件下制备的样品结晶度最好。当前驱液的pH=5.7时,激发光谱中的Eu-O电荷迁移带的峰位波长最大(262 nm),这可能是由于在此条件下合成的样品中Eu-O键长最长。发射光谱表明:当前驱液的pH>5.7时,Eu3+的发射光谱中的红橙比(I614/I589)随pH值的增大而增大,且当前驱液的pH值在5.7~6.9区间,红橙比(I614/I589)随pH值的增大的速率要比pH值在6.9~9.3之间增加的速率要快。另外,随着pH值的增大,样品的发光强度呈先增大后减小的变化趋势。当前驱溶液pH=8.1时,样品的发光强度最大。 The samples of 2ZnO·2.2B2O3·3H2O: Eu3+ were prepared by hydrothermal method by adjusting the pH value of precursor solution with the ammonia.The crystal phase and luminescent properties of the samples were characterized by X-ray diffraction(XRD) and fluorescence spectrometer.The results of XRD analysis showed that the degree of crystallization of the samples was influenced by the concentration of pH value in precursor solution.The samples were crystallized best when the pH value was around 7.The excitation spectra showed that the charge transfer band of Eu-O located at 262 nm when pH=5.7.This may be due to the band length of Eu-O which is the longest when pH=5.7.The intensity ratio of the emission bands at 614 nm and 589 nm(I614/I589) increased as the pH value(pH〉5.7) increasing.Meanwhile,the ratios of I614/I589 of the samples synthesized in the condition of pH=5.7-6.9 increased faster than samples synthesized in the condition of pH=6.9-9.3.The emission spectra showed that the emission intensity of Eu3+ of the sample synthesized at pH=8.1 was the strongest.
出处 《人工晶体学报》 EI CAS CSCD 北大核心 2012年第3期661-665,共5页 Journal of Synthetic Crystals
基金 国家自然科学基金(11004153) 广东省自然科学基金(10152902001000009) 广东省科技计划项目(2009B030803015) 2011年广东省高等学校人才引进专项资金(粤财教[2011]431号)
关键词 水热法 PH值 发光强度 hydrothermal; pH value; luminescence intensity
  • 相关文献

参考文献16

  • 1汤珅,黄妙良,杨纪元,玉富达,商光禄,吴季怀.YVO4:Eu^3+纳米荧光粉的水热法合成及其光致发光性能的研究[J].人工晶体学报,2011,40(6):1429-1434. 被引量:8
  • 2Leskel M, Saakes M, Blasse G. Energy Transfer Phenomena in GdMgB5 O10 [ J ]. Materials Research Bulletin, 1984,19 (2) : 151-159.
  • 3Wang Y, Endo T, He L, et al. Sythesis and Photoluminescence of Eu^3+ -Doped (Y, Gd)BO3 Phosphors by a Mild Hydrothermal Process [ J ]. J. Crys. Growth,2004,265( 3-4 ) :568-574.
  • 4Kim D S, Lee R Y. Synthesis and Photoluminescence Properties of (Y,Gd)BO3: Eu Phosphor Prepared by Ultrasonic Spray[J]. J. Mater. Sci. , 2000,35 (19) :4777-4782.
  • 5Cui X Z, Zhuang W D, Yu Z J, et al. Preparation of Red Phosphor (Y, Gd)BO3: Eu by Soft Chemistry Methods[ J]. J. Alloys Compounds, 2008,451 ( 1-2 ) :280-285.
  • 6李敏,刘家祥,杨儒,陈坚,叶增.红色荧光粉Sr_2MgSi_2O_7:Eu^(3+)的合成及发光性能[J].硅酸盐学报,2011,39(9):1379-1383. 被引量:9
  • 7Zhou Y H, Lin J, Wang S B, et al. Preparation of Y3 A15 O12: Eu Phosphors by Citric-Gel Method and Their Luminescent Properties [ J ]. Opt. Mater. , 2002,211 : 13-20.
  • 8王晓纯,任博,郭常新,姜桂铖,尹民.Y_2O_3:Er^(3+)的共沉淀法制备和pH值对发光性质的影响[J].光谱学与光谱分析,2011,31(3):612-616. 被引量:2
  • 9Yu L X, Li D C, Yue M X, et al. Dependence of Morphology and Photolumineseent Properties of GdPO4 : Eu^3 + Nanostruetures on Synthesis Condition [ J ]. Chem. Phys. , 2006,326 ( 2 -3 ) : 478 -482.
  • 10Wang Y H, Zuo Y Y, Gao H. Luminescence Properties of Nanocrystalline YV04: Eu^3+ under UV and VUV Excitation [ J ]. Mater. Res. Bull. , 2006,41:2147-2153.

二级参考文献69

共引文献31

同被引文献10

引证文献2

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部