CaF_2对硫铝酸锶钙水泥矿物形成及水化过程的影响 被引量:2

Effect of CaF_2 on Process of Mineral Formation and Hydration of Calcium Strontium Sulphoaluminate Cement
下载PDF
导出
摘要 测试了掺CaF2硫铝酸锶钙水泥的抗压强度.通过热分析、X射线衍射分析和扫描电子显微镜观察,研究了CaF2对硫铝酸锶钙水泥熟料矿物形成和水化过程的影响.结果表明,当CaF2掺量为0.2%(质量分数)时,硫铝酸锶钙水泥抗压强度最高,3,28d抗压强度分别达到65.0,86.2MPa.在水泥煅烧过程中,CaF2能加速CaCO3的分解及C1.50Sr2.50A3珔S矿物的形成.此外,CaF2可以加快硫铝酸锶钙水泥的水化速率并促使水化产物CAH10转化为C3AH6. The compressive strength of calcium strontium sulphoaluminate cement with CaF2 added was tested. The influence of CaF2 on process of mineral formation and hydration of calcium strontium sul-phoaluminate cement were studied by thermal analysis(DTA-TG), X-ray diffraction(XRD) and scanning electron microscopy(SEM). The results show that compressive strength of calcium strontium sulphoalumi-nate cement with 0.2 % ( by mass) of CaF2 added is optimal, the compressive strength for 3,28 d is 65.0, 86.2 MPa respectively. CaF2 accelerates decomposition of CaCO3 and formation of C1.50 Sr2.50 A3^-S during sintering of clinker. Due to CaF2, hydration rate of cement is speeded up and CAH10 changes to C3AH6.
出处 《建筑材料学报》 EI CAS CSCD 北大核心 2012年第3期377-381,共5页 Journal of Building Materials
基金 国家973前期研究专项(2010CB635117)
关键词 硫铝酸锶钙水泥 CAF2 水化 强度 calcium strontium sulphoaluminate cement CaF2 hydration strength
  • 相关文献

参考文献5

二级参考文献24

  • 1阎培渝.3CaO·3Al_2O_3·SrSO_4浆体结构与强度的关系[J].武汉工业大学学报,1994,16(1):19-22. 被引量:8
  • 2冯修吉,闵新民,陶从喜.应用量子化学算法研究硅酸二钙的结构与性能[J].武汉工业大学学报,1994,16(2):1-6. 被引量:19
  • 3龙世宗,廖广林,赵三银.硫铝酸钡钙矿物烧成若干问题的研究[J].中国建材科技,1996,5(3):11-16. 被引量:4
  • 4廖广林.3CaO·3Al2O3·CaSO4及其衍生物的结构与性能研究[M].武汉:武汉工业大学,1987..
  • 5张文生.3CaO·3Al2O3·BaSO4的特性、应用及其机理研究[M].武汉:武汉工业大学,1998..
  • 6段长强 孟庆芳 等.现代化学试剂目录手册[M].北京:化学工业出版社,1986.160.
  • 7李德栋.硫铝酸盐水泥的红外光谱研究[J].硅酸盐学报,1984,12(1):119-125.
  • 8程新.3Cao·3Al2O3·SrSO4的结构与特性和计算量子化学在一些水泥熟料矿物中的应用[博士学位论文].武汉:武汉工业大学,1994..
  • 9程新,博士学位论文,1994年
  • 10冯庆革,硕士学位论文,1994年

共引文献59

同被引文献10

引证文献2

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部