针对锡含量为8%~12%的锡青铜合金脆性大、难以通过塑性变形实现较高致密度的问题,采用包套挤压工艺制备新型耐磨Cu-Sn-Pb-Ni合金,分析其铸态及包套挤压态的微观组织及性能。包套挤压的密度和硬度分别达到8.98g/cm3和HB135.7;挤压后合金抗拉强度和伸长率分别为345.366MPa和11.4%。结果表明,合金在外加包套作用下塑性有所提高。
Directing to the difficulties in the densification of Cu-Sn-Pb-Ni alloy containing 8%~12% tin by conventional plastic forming,the plastic deformation of Cu-Sn-Pb-Ni alloy was carried out by the canning extrusion process.The microstructure and properties of as-cast alloy and as-extruded alloy were analyzed.The as-extruded alloy with the density of 8.98g/cm3 and strength of 345MPa was obtained.The results reveal that the properties of the Cu-Sn-Pb-Ni alloy can be improved via the canning extrusion process.