Fatigue crack initiation for Al-Zn-Mg alloy welded joint 被引量:2

Fatigue crack initiation for Al-Zn-Mg alloy welded joint
原文传递
导出
摘要 To investigate fatigue crack initiation characteristics of A1-Zn-Mg alloy welded joint, notched specimens were used in fatigue test for the base metal, welding bead and heat affected zone (HAZ). The fatigue fracture surface near the fatigue crack initiation site was observed by scanning electron microscope (SEM). The results show that the differences of fatigue crack initiation life among base metal, welding bead and HAZ are not obvious. Inhomogeneity in microstructure and mechanical performance of HAZ influences the fatigue crack initiation life. The ratio of fatigue crack initiation life (Ni) to fatigue failure life (Nf) for the base metal, welding bead and HAZ of A7N01 aluminium alloy welded joint are 26.32%, 40.21% and 60.67%, respectively. Fatigue crack initiation life can be predicted using a uniform model. Observation of fatigue fracture surfaces shows that for the welding bead a fatigue crack initiates from the smooth surface due to the welding process, the blowhole in HAZ causes fatigue crack and the crushed second phase particles play an important role in fatigue crack initiation for the base metal. To investigate fatigue crack initiation characteristics of A1-Zn-Mg alloy welded joint, notched specimens were used in fatigue test for the base metal, welding bead and heat affected zone (HAZ). The fatigue fracture surface near the fatigue crack initiation site was observed by scanning electron microscope (SEM). The results show that the differences of fatigue crack initiation life among base metal, welding bead and HAZ are not obvious. Inhomogeneity in microstructure and mechanical performance of HAZ influences the fatigue crack initiation life. The ratio of fatigue crack initiation life (Ni) to fatigue failure life (Nf) for the base metal, welding bead and HAZ of A7N01 aluminium alloy welded joint are 26.32%, 40.21% and 60.67%, respectively. Fatigue crack initiation life can be predicted using a uniform model. Observation of fatigue fracture surfaces shows that for the welding bead a fatigue crack initiates from the smooth surface due to the welding process, the blowhole in HAZ causes fatigue crack and the crushed second phase particles play an important role in fatigue crack initiation for the base metal.
出处 《Acta Metallurgica Sinica(English Letters)》 SCIE EI CAS CSCD 2012年第3期235-240,共6页 金属学报(英文版)
关键词 A1-Zn-Mg alloy Welded joint Fatigue crack initiation Life pre- diction A1-Zn-Mg alloy Welded joint Fatigue crack initiation Life pre- diction
  • 相关文献

参考文献1

二级参考文献11

  • 1M. Cilense,W. Garlipp,A. T. Adorno,C. S. Louren?o.Influence of the heat treatment and of the chromium addition on the precipitation phenomena of AI-Zn-Mg-Cu alloy[J]. Journal of Materials Science Letters . 1995 (4)
  • 2N. A. Razik.Precise lattice constants of the T and α phases in an Al-Zn-Mg alloy[J]. Journal of Materials Science Letters . 1985 (10)
  • 3G. Honyek,I. Kovács,J. Lendvai,Ng-Huy-Sinh,T. Ungár,H. L?ffler,R. Gerlach.The influence of Mg content on the formation and reversion of Guinier-Preston zones in Al-4.5 at % Zn-x Mg alloys[J]. Journal of Materials Science . 1981 (10)
  • 4A. Juhász,P. Tasnádi,I. Kovács,T. Ungár.Mechanical properties of Al-Zn-Mg alloys investigated by microhardness measurements[J]. Journal of Materials Science . 1981 (2)
  • 5M. Radomsky,O. Kabisch,H. L?ffler,J. Lendvai,T. Ungár,I. Kovács,G. Honyek.On the decomposition behaviour of Al-4.5 at% Zn-2 to 3 at% Mg alloys during continuous heating[J]. Journal of Materials Science . 1979 (12)
  • 6T. Ungár,J. Lendvai,I. Kovács,G. Groma,E. Kovács-Csetényi.The decomposition of the solid solution state in the temperature range 20 to 200° C in an Al-Zn-Mg alloy[J]. Journal of Materials Science . 1979 (3)
  • 7J.Yan,C.Z.Li and M.G.Yan: J. MAter. Science . 1992
  • 8J.R.Pickens and T.J.Langan: Metall. Transactions . 1987
  • 9J.K.Park and A.J.Ardell: Metall. Transactions . 1983
  • 10C.H.J.Davies,N.Raghunathan and T.Sheppard: ActaMetall. Mater . 1994

共引文献4

同被引文献7

引证文献2

二级引证文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部