Q390钢焊接CCT曲线的测定 被引量:8

Measurement of Q390 steel welding CCT curve
下载PDF
导出
摘要 模拟Q390钢焊接工况,利用热膨胀法通过Gleeble1500热模拟机测定Q390钢的连续冷却转变曲线(CCT曲线).采用光学显微镜、扫描电镜对不同冷却速度下的试样进行显微组织观察及分析,通过对Q390钢连续冷却特性的分析和比较得出Q390钢的SH-CCT曲线.结果表明,SH-CCT曲线分为3个区域,高温区的铁素体+珠光体转变区,中温区内的贝氏体转变区,低温区的马氏体转变区.在0.015~0.1℃/s的冷却速度范围内获得铁素体+珠光体+粒状贝氏体的整合组织;在0.5~1℃/s冷却速度范围内有大量的粒状贝氏体组织生成;当冷却速度大于25℃/s时,有马氏体与残余奥氏体整合组织生成. By simulating Q390 steel welding condition,by means of thermal-dilatometer,continuous cooling transformation curve of Q390 steel was measured by Gleeble1500 thermal-simulator,at the same time,the microstructure of different cooling velocity was observed and analyzed by OM and SEM.SH-CCT curve was obtained through continuous cool character analysis and contrast.The results show that phase transformation region contains three parts:the ferrite and pearlite transition zone at high temperature,the bainite transition zone at moderate temperature and the martensite transition zone at low temperature.The microstructure including ferrite,pearlite and granular bainite can be obtained when the cooling velocity is between 0.015 and 0.1 ℃/s;lots of bainite structure can be obtained at 0.5-1 ℃/s cooling rate range;the martensite and residual austenite microstructure be obtained when the cooling velocity is beyond 25 ℃/s.
出处 《焊接学报》 EI CAS CSCD 北大核心 2012年第7期57-60,116,共4页 Transactions of The China Welding Institution
基金 国防民口配套项目(115-4-1465)
关键词 Q390钢 热模拟 焊接CCT曲线 Q390 steel thermal-simulation SH-CCT
  • 相关文献

参考文献9

二级参考文献36

共引文献86

同被引文献40

引证文献8

二级引证文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部