研究AZ31镁合金挤压板材在473~523K的温度范围内。应变速率0.001~1.0s-1压缩时的流变应力行为,计算板材沿挤压方向压缩时的激活能,并结合光学显微镜和透射电子显微镜探讨合金软化机制和变形机理之间的联系。结果表明,在中温下沿挤压方向压缩时,AZ31挤压态镁合金的变形激活能为174.18kJ/mol。这说明,由热激活位错交滑移所控制的动态再结晶是合金中温变形的主要软化机制。位错滑移是中温变形的主要变形机理,而孪生的作用则不大。其主要的动态再结晶机制为持续动态再结晶,并伴随少量的孪生动态再结晶。
The flow stress behavior of extruded AZ31 magnesium alloy sheet was investigated by means of compression tests at temperatures between 473 and 523 K and strain rates ranging from 0.001 to 1.0 s-1. The deformation activation energy of the sheet in extrusion direction (ED) was calculated, and the relationship between the softening effect and deformation mechanism was elucidated by optical microscopy and transmission electron microscopy. The results show that when the extruded AZ31 magnesium alloy samples were compressed at moderate temperatures in ED direction, the deformation activation energy is 174.18 kJ/mol, which means that dynamic recrystallization (DRX) is the main softening effect and is controlled by cross slip of thermal active dislocation. Dislocation slip is the main deformation mechanism in moderate-temperature deformation process except twinning. The main DRX effect at moderate temperatures can be considered to be continuous dynamic recrystallization accommodated with twinning DRX.
基金
Project (50804015) supported by the National Natural Science Foundation of China
Project (GJJ11162) supported by the Youth Science Foundation of Jiangxi Educational Committee,China
Project (EA201001035) supported by the Doctor Startup Foundation of Nanchang Hangkong University,China
关键词
AZ31镁合金
变形机理
激活能
动态再结晶
AZ31 magnesium alloy
deformation mechanism
active energy
dynamic recrystallization