摘要
本文研究了电子束辐照降解固态羧甲基纤维素(CMC)效应。结果表明:辐照CMC固体样品配制2%水溶液粘度随着辐照剂量增大而减少;红外光谱分析表明,辐照导致CMC分子链上糖苷键C1-O-C4断裂。固态CMC辐照降解符合无规则降解动力学规律。
In this work, electron beam degradation of carboxymethyl cellulose (CMC) in solid state was investigated. The results showed that viscosity of the irradiated CMC in 2% aqueous solution decreased with increasing doses. FT-IR characterization of the CMC samples before and after irradiation showed that the irradiation of 40 kGy can lead to rapid breaking off of the glucoside bond (C1-O-C4). The irradiation degradation of CMC in solid state obeys the rule of random degradation.
出处
《核技术》
CAS
CSCD
北大核心
2012年第7期512-514,共3页
Nuclear Techniques
基金
安徽省教育厅科学研究项目(KJ2011Z363)
黄山学院校级科研项目(2011xkj004)资助
关键词
羧甲基纤维素
电子束辐照
粘度
Carboxymethyl cellulose (CMC), Electron beam Irradiation, Viscosity