针对双向拉伸聚丙烯薄膜(BOPP)包装材料,制备低热封丙烯酸乳液涂层材料.通过考察聚合工艺,调节单体比例、乳化剂、引发剂及其用量,测定乳液性能.研究结果表明:以十二烷基硫酸钠(K12)作为乳化剂,其适中的质量分数为0.5%,以质量分数为0.5%的过硫酸铵作为引发剂,软硬单体按质量比为1∶1混合,进一步加入质量分数为2%的功能性单体丙烯酸(AA),所制备的乳液稳定性较好,成膜性优异,热封强度达到2.64 N/cm,大大超过现有市场产品的性能.
The acylic emulsion with low heat sealing performance is synthesized for double oriented polypropylene film (BOPP) packaging materials. The effect of polymerization process, ration of monomer content, emulsifier, initiator and its content on emulsion performance are taken into account. The results are showed that: the sodium lauryl sulfate (K12) with a total mass account of 0.3% is properly used as emulsifier, ammonium persulfate with 0.5% content is used as initiator; The appropriate ration of hard and soft monomers is 1:1. By adding 2% acrylic acid (AA), the emulsion enjoys a good adhesion with BOPP, while the peel strength reached 2.64 N/cm.
出处
《南通大学学报(自然科学版)》
CAS
2012年第2期47-51,共5页
Journal of Nantong University(Natural Science Edition)
基金
江苏省高校自然科学基金项目(09KJD430008)
南通大学引进人才启动费项目(09R03)
南通市应用研究计划项目(BK2011033)
关键词
聚丙烯酸酯
乳液聚合
包装材料
低热封
polyacrylate
emulsion polymerization
packaging material
low heat sealing