梅山铁尾矿强磁再选粗精矿深度还原试验 被引量:4

Research on Deep Reduction of Reelection Coarse Concentrate After High Intensity Magnetie Separation of Meishan Iron Tailings
下载PDF
导出
摘要 由于梅山铁矿石中弱磁性铁矿物含量很高,导致梅山尾矿的铁品位较高。梅山铁矿选矿厂对该尾矿进行了强磁再选,获得了铁品位为31.80%的再选粗精矿。为获得合格的铁产品,东北大学对该再选粗精矿进行了深度还原工艺技术条件研究,结果表明,在还原温度为1 275℃,还原时间为60 min,料层厚度为30 mm,配碳系数为2.0,煤粉粒度为-2.0 mm情况下进行深度还原,金属化率为89.20%的还原物料经1段弱磁选可获得铁品位为80.05%、回收率为98.03%的弱磁选铁粉。 Iron content of Meishan tailings is relatively high,because of high content of weakly magnetic iron minerals in Meishan iron ore.These tailings were treated by Meishan iron concentrator using high intensity magnetic separation,and re-concentrate with 31.80% iron grade were produced.Then deep reduction was used to treat reelection coarse concentrate.The results show that the reduced materials with metallization rate up to 89.20% was obtained under the optimal deep reduction conditions such as reducing temperature 1 275 ℃,reducing time 60 min,thickness of material 30 mm and carbon coefficient 2.0.Iron powder with a TFe grade 80.05% at an iron recovery 98.03% was achieved after one-stage low intensity magnetic separation.
出处 《金属矿山》 CAS 北大核心 2012年第7期148-150,共3页 Metal Mine
基金 国家高技术研究发展计划(863计划)项目(编号:2012AA062401)
关键词 强磁再选粗精矿 铁尾矿 深度还原 金属化率 Reelection coarse concentration after high intensity magnetic separation Iron tailings Deep reduction Metallization degree
  • 相关文献

参考文献2

二级参考文献11

  • 1车丽萍,余永富.我国稀土矿选矿生产现状及选矿技术发展[J].稀土,2006,27(1):95-102. 被引量:61
  • 2李伟强,顾连兴,唐俊华,郑远川,吴昌志.江西武山块状硫化物矿石表生风化过程中稀土元素地球化学行为[J].中国稀土学报,2006,24(3):350-356. 被引量:8
  • 3吕振福 韩跃新 印万忠 等.东鞍山含碳酸盐铁矿石浮选新工艺研究.矿冶工程,2008,28(6):7-10.
  • 4Kanazawa Y, Karnitani M. Rare earth minerals and resources in the world[J]. Journal of Alloys and Compounds, 2006, 41 (9) :13390 1343.
  • 5Yuan Z F, Wang X Q, Xu C, et al. A new process for comprehensive utilization of complex titania ore[J]. Minerals Engineering, 2006,19 (9) : 975 - 978.
  • 6Qi H W, Hu R Z, Zhang Q. REE geochemistry of the cretaceous lignite from Wulantuga germanium deposit, Inner Mongolia, Northeastern China[J ]. International Journal of Cool Geology, 2007,71 (2) : 329 - 344.
  • 7Fortini O. Renewable energy steelmaking on a new process for ironmaking[D]. Pittsburgh; Carnegie Mellon University, 2003.
  • 8Kamijo C, Hoshi M, Kawaguchi T, et al. Production of direct reduced iron by a sheet material inserting metallization method[J]. ISIJ Int, 2001,41(S):13 -16.
  • 9Snwa Y, Yamamoto T, Takeda K, et al. New coal-based process to produce high quality DRI for the EAF[ J]. ISU Int, 2001,41(S) :17- 21.
  • 10Narcin N, Aydin S, Sesen K, et al. Reduction of iron ore pellets with domestic lignite coal in a rotary tube fumace[J ]. Int J Miner Process, 1995,43(S) :49 - 59.

共引文献49

同被引文献97

引证文献4

二级引证文献28

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部