摘要
2205 duplex stainless steels （ DSSs） are welded in gas tungsten arc welding （GTAW） with the addition of N2 to argon, and the desirable microstructure and properties of the joints are obtained by altering the nitrogen percentage in the shielding gas mixture. The mechanical properties of joints are tested with tensile and microhardness machine, and the joint micrustructure is analyzed with scanning electron microscope （SEM） and optical microscope （ OM ） , and detrimental phase precipitate is investigated with X-ray diffraction （XRD）, respectively. Finally, the corrosion behaviour of joint is also evaluated. Results show that the favorable joint strength and corrosion resistance can be obtained with appropriate shielding gas mixture in GTA W. No detrimental phase precipitates in the weldment, and the joint tensile fracture obviously presents the characteristic of ductile fracture.
2205 duplex stainless steels （ DSSs） are welded in gas tungsten arc welding （GTAW） with the addition of N2 to argon, and the desirable microstructure and properties of the joints are obtained by altering the nitrogen percentage in the shielding gas mixture. The mechanical properties of joints are tested with tensile and microhardness machine, and the joint micrustructure is analyzed with scanning electron microscope （SEM） and optical microscope （ OM ） , and detrimental phase precipitate is investigated with X-ray diffraction （XRD）, respectively. Finally, the corrosion behaviour of joint is also evaluated. Results show that the favorable joint strength and corrosion resistance can be obtained with appropriate shielding gas mixture in GTA W. No detrimental phase precipitates in the weldment, and the joint tensile fracture obviously presents the characteristic of ductile fracture.