摘要
A fibrous strong base anion exchanger （QAPPS） was prepared for the first time via chloromethylation and quaternary amination reaction of polyphenylene sulfide fiber （PPS）, and its physical-chemical structure and adsorption behavior for Cr（VI） were characterized by FT- IR, Energy Dispersive Spectrometry, TG-DTG, elemental analysis and batch adsorptive technique, respectively. The novel fibrous adsorbent could effectively adsorb Cr（VI） over the pH range 1-12, the maximum adsorption capacity was 166.39 mg/g at pH 3.5, and the adsorption behavior could be described well by Langmuir isotherm equation model. The adsorption kinetics was studied using pseudo first-order and pseudo second-order models, and the 4/2 and equilibrium adsorption time were 5 and 20 min respectively when initial Cr（VI） concentration was 100 mg/L. The saturated fibers could be regenerated rapidly by a mixed solution of 0.5 mol/L NaOH and 0.5 mol/L NaCl, and the adsorption capacity was well maintained after six adsorption-desorption cycles.
A fibrous strong base anion exchanger （QAPPS） was prepared for the first time via chloromethylation and quaternary amination reaction of polyphenylene sulfide fiber （PPS）, and its physical-chemical structure and adsorption behavior for Cr（VI） were characterized by FT- IR, Energy Dispersive Spectrometry, TG-DTG, elemental analysis and batch adsorptive technique, respectively. The novel fibrous adsorbent could effectively adsorb Cr（VI） over the pH range 1-12, the maximum adsorption capacity was 166.39 mg/g at pH 3.5, and the adsorption behavior could be described well by Langmuir isotherm equation model. The adsorption kinetics was studied using pseudo first-order and pseudo second-order models, and the 4/2 and equilibrium adsorption time were 5 and 20 min respectively when initial Cr（VI） concentration was 100 mg/L. The saturated fibers could be regenerated rapidly by a mixed solution of 0.5 mol/L NaOH and 0.5 mol/L NaCl, and the adsorption capacity was well maintained after six adsorption-desorption cycles.
基金
support of the National Natural Science Foundation of China (No. 20574063,21004055)