摘要
The low temperature sample stage in a transmission electron microscope is used to investigate the charge ordering behaviours in a Bi0.4Ca0.6MnO3 film with a thickness of 110 nm at 103 K. Six different types of superlattice structures are observed using the selected-area electron diffraction （SAED） technique, while three of them match well with the modulation stripes in high-resolution transmission electron microscopy （HRTEM） images. It is found that the modulation periodicity and direction are completely different in the region close to the Bi0.4Ca0.6MnO3/SrTiO3 interface from those in the region a little further from the Bi0.4Ca0.6MnO3/SrTiO3 interface, and the possible reasons for this are discussed. Based on the experimental results, structural models are proposed for these localized modulated structures.
The low temperature sample stage in a transmission electron microscope is used to investigate the charge ordering behaviours in a Bi0.4Ca0.6MnO3 film with a thickness of 110 nm at 103 K. Six different types of superlattice structures are observed using the selected-area electron diffraction （SAED） technique, while three of them match well with the modulation stripes in high-resolution transmission electron microscopy （HRTEM） images. It is found that the modulation periodicity and direction are completely different in the region close to the Bi0.4Ca0.6MnO3/SrTiO3 interface from those in the region a little further from the Bi0.4Ca0.6MnO3/SrTiO3 interface, and the possible reasons for this are discussed. Based on the experimental results, structural models are proposed for these localized modulated structures.
基金
Project supported by the National Natural Science Foundation of China (Grant Nos. 10974105 and 50832007)
the Project of Introducing Talents to Support Thousand Talents Programs,China (Grant No. P201101032)
the Program of Upgrading Technology for Scientific Instruments in Shandong Province,China (Grant No. 2011SJGZ16)
the Program of Science and Technology in Qingdao City,China (Grant No. 11-2-4-23-hz)