We investigated photoluminescence characteristics of silicone oils treated by C2F6 and CHF3 plasma. The silicone oil treated by the C2F6 plasma emitted a white light mainly composed of 415 nm, 469 nm, and 554 nm emissions, while that treated by the CHF3 plasma emitted a pink light （415 nm）. Fourier transformed infrared spectroscopy and Raman spectroscopy studies showed that the photoluminescence was correlated with the Si-C bond, the carbon-related defects and the oxygen vacancies. It was suggested that the light emitting at 554 nm was related to the Si-C bond and the carbon-related defects, while the pink emission at 415 nm was related to the oxygen vacancies.
We investigated photoluminescence characteristics of silicone oils treated by C2F6 and CHF3 plasma. The silicone oil treated by the C2F6 plasma emitted a white light mainly composed of 415 nm, 469 nm, and 554 nm emissions, while that treated by the CHF3 plasma emitted a pink light （415 nm）. Fourier transformed infrared spectroscopy and Raman spectroscopy studies showed that the photoluminescence was correlated with the Si-C bond, the carbon-related defects and the oxygen vacancies. It was suggested that the light emitting at 554 nm was related to the Si-C bond and the carbon-related defects, while the pink emission at 415 nm was related to the oxygen vacancies.
基金
Project supported by the National Natural Science Foundation of China (Grant Nos.10975105 and 11075114)