VN微合金化Q460D中厚板生产试制

Trial Production of VN-Microalloying Q460D Medium Plate
下载PDF
导出
摘要 利用VN微合金工艺进行Q460D中厚板的试制,通过对钢板化学成分、冶炼和连铸工艺、轧制及冷却工艺的合理设计,成功试制出60mm以上规格Q460D钢板,其屈服强度为460~515MPa、抗拉强度为600-650MPa、-20℃低温冲击吸收功均值为140~200J,具有较高的强度和良好的低温冲击韧性,满足QS00D的标准要求。 The trim production of VN-microalloying Q460D medium plate was introduced in this paper. The more than 60ram thick steel plate of Q460 was successfully manufactured by proper design of its chemical composition, smelting process, continuous casting process, rolling and cooling process. Tits yield strength was 460 - 515 MPa and tensile strength was 600 - 650 MPa. The average impact energy at -20℃ was 140 - 200 J. It is shown that this trial steel has high strength and good low-temperature impact toughness, which could meet the standard requirements of Q500D.
机构地区 首钢技术研究院
出处 《首钢科技》 2012年第4期32-34,共3页 Shougang Science and Technology
关键词 VN微合金 Q460D 中厚板 试制 VN- microalloying, Q460D, medium plate, trail production
  • 相关文献

参考文献4

二级参考文献10

共引文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部