采用共沉淀法制备了细的Ce0.8Y0.2O1.9(YDC)粉末,并将其应用于钴掺杂的YDC电解质材料。研究了钴元素对材料烧结性能和电性能的影响。结果表明,钴元素显著增加了材料的密度(烧结温度在1000℃时,其密度超过理论密度的98%)和电导率(750℃时0.99S/m),同时还发现小于1μm尺寸的晶粒具有高的电导率。
Fine Ce0. 8 Y0. 2 O1.9 (Y D C) powders were prepared by chemical co-precipitation. The cobah-doped YDC electrolytes were prepared by a solid state reaction route. The effect of cobalt ions on the sinterability and electrical conductivity was investigated. Cobalt ions increase the density (over 98% theoretical density at sintering temperature of 1000℃) and electrical conductivity (0. 99 S/m at 750℃in air). The results also reveal that a smaller grain size (less than 1μm) correlates with a higher conductivity.