摘要
采用水热法合成了可见光催化剂AgSbO3,以直接耐酸大红4BS染料废水为目标污染物,研究前驱物pH、水热合成温度以及水热合成时间对催化剂的可见光催化活性和晶型等方面的影响,通过XRD和SEM进行表征。结果表明,在原始pH、和80℃水热合成12 h条件下的AgSbO3活性最好,对目标污染物的降解率达到94.3%。
A new type of visible-light-driven photocatalyst AgSbO3 was prepared by hydrothermal synthesis method. The influence of pH values of the precursor, hydrothermal synthetic temperature and time on photoeatalytic activities of AgSbO3 catalysts for the degradation of direct fast scarlet(4BS) dye wastewater was investigated. The as-prepared photoeatalysts were characterized by XRD and SEM. The results showed that AgSbO3 catalyst hydrothermally synthesized under original pH value and 80 ℃ for 12 h exhibited the highest photocatalytic activity, and the deeoloration rate for 4BS dye wastewater over AgSbO3 catalyst under this condition reached 94.3%.
出处
《工业催化》
CAS
2012年第8期31-34,共4页
Industrial Catalysis
关键词
催化化学
水热合成
可见光催化
AgSbO3
4BS染料废水
catalytic chemistry
hydrothermal synthesis
visible light photocatalysis
AgSbO3
4BS dye wastewater