Crystallization of Calcium Oxalate on the Self-assembled Monolayer of L-Cysteine
下载PDF
导出
摘要 在CaCl2.H2O和Na2C2O4配制的过饱和溶液中,利用L-半胱氨酸(L-Cys)在金片上形成的自组装膜为模板,研究了草酸钙(CaOxa)在自组装膜上的结晶行为,并探讨了溶液pH对CaOxa晶体组成、晶型及其形貌的影响。采用X射线衍射(XRD)和扫描电子显微镜(SEM)等技术对CaOxa晶体的结构和形貌进行了表征。实验结果表明:当溶液pH=3.0时,溶液中可以形成一水草酸钙(CaC2O4.H2O,COM)和二水草酸钙(CaC2O4.2H2O,COD)晶体,而在同样pH条件下,在L-Cys自组装膜上只形成COD晶体,表明自组装单层对CaOxa晶体的成核和生长有重要影响。通过改变溶液的pH,在自组装单层上可以得到不同晶型和不同形状的CaOxa晶体。当pH=3.0时得到四方块状的COD晶体,而pH=5.0和pH=7.0时分别得到六边形和拉长六边形的COM晶体。 In order to study the interaction between the organic molecules and calcium oxalate crystals, the self- assembled monolayer of L-cysteine was used as the template to induce the crystallization of calcium oxalate. The calcium oxalate crystals obtained from the solution and on the monolayer of L-cysteine were characterized by X-ray powder diffraction (XRD) and scanning electron microscopy (SEM). Experimental results indicated that the self-assembled monolayer of L-Cys has a strong impact on the crystallization of CaOxa. Various crystal morphotogies such as square, hexagon, elongated hexagon were obtained. With the increase of the solution pH, the crystals obtained on the monolayer of L-Cys were shifted from calcium oxalate dihydrate at pH=3.0 to calcium oxalate hydrate at pH=7.0.
出处 《无机化学学报》 SCIE CAS CSCD 北大核心 2012年第10期2160-2164,共5页 Chinese Journal of Inorganic Chemistry
基金 国家自然科学基金(No.20873136)资助项目
关键词 草酸钙 晶体 自组装膜 诱导 calcium oxalate crystal self-assembled monolayer induction
  • 引文网络
  • 相关文献

参考文献26

  • 1Ouyang J M, Zheng H, Deng S P. J. Cryst. Growth, 2006, 293:118-123.
  • 2Qiu S R, Wierzbicki A, Salter E A, et al. J. Am. Chem. Soc., 2005,127:9036-9044.
  • 3Sargut S T, Sayan P, Kiran B. J. Cryst. Res. Technol., 2010, 45:31-38.
  • 4YUHai-Yan(于海燕),ZHANGHui-Min(张惠敏),OUYANGJian-Ming(欧阳健明).J. Chin. Electron Microsco. Soc.(Dianzi Xianwei Xuebao), 2007,26(1):44-48.
  • 5LuPeng(鲁鹏),HOUShan-Hua(侯善华),OUYANGJian.Ming(欧阳健明).Chinese J. Inorg. Chem. (Wuji Huaxue Xuebao), 2010,26(1):17-24.
  • 6Fischer V, Landfester K, Muoz-Esp R. J. Cryst. Growth Des., 2011,11:1880-1890.
  • 7Wang L J, Qiu S R, Zachowiez W, et al. Langmuir, 2006, 22:7279-7285.
  • 8Sargut S T, Sayan P, Kiran B. J. Cryst. Res. Technol., 2009, 44:807-817.
  • 9XIERons(谢蓉),YANGJin(杨锦),WANMu-Hua(万牡华),et al. Chinese J. lnorg. Chem.(Wuji Huaxue Xuebao), 2010, 26(4):560-566.
  • 10Jung T, Sheng X X, Choi C K, et al. Langmuir, 2004,20: 8587-8596.

同被引文献25

  • 1SCHMIDT I, LEE K, ZOLOTOYABKO E, et al. Nanocrystalline calcitic lens arrays fabricated by self-assembly followed by amorphous-to-crystal- line phase transformation[J]. Acs Nano, 2014, 8(9) : 9233 -9238.
  • 2ROINE J, TENHO M, MURTOMAA M, et al. X-ray texture analysis of paper coating pigments and the correlation with chemical composition anal- ysis[J]. J Appl Phys, 2007, 102: 083530.
  • 3CHEN B, EVANS J R G. Impact strength of polymer-clay nanocomposites[ J]. Soft Matter, 2009, 5:3572 -3584.
  • 4RESNIK D, VRTACNIK D, ALJANCIC U, et al. Mieromachined crystal plane on (100) and (110) silicon for optical mirror applications[ J]. Proceedings of the SPIE-The International Society for Optical Engineering, 2004, 5276 ( 1 ) : 489 - 497.
  • 5CUI X Z, ZHANG T C, MEI Z X, et al. Growth of single-crystalline ZnO film with two-dimensional periodic structure on Si ( 111 ) substrate by molecular beam epitaxy[J]. J Cryst Growth, 2008, 310(24) : 5428 -5431.
  • 6ZHU Z H, TONG H, REN Y Y, et al. Meretrix lusoria-a natural biocomposite material: In situ analysis of hierarchical fabrication and micro-hard- ness[J]. Micron, 2006, 37(1) : 35 -40.
  • 7SUDO S, FUJIKAWA T, NAGAKURA T, et al. Structures of mollusc shell framework proteins[ J]. Nature, 1997, 387:563 -564.
  • 8SUZUKI M, SARUWATARI K, KOGURE T, et al. An acidic matrix protein, Pif, is a key macromolecule for nacre formation [ J ]. Science, 2009, 325(5946) : 1388 - 1390.
  • 9WOLF S E, LOGES N, MATHIASCH B, et al. Phase selection of calcium carbonate through the chirality of adsorbed amino acids[ J ]. Angew Chem Int Ed, 2007, 46(29) : 5618 -5623.
  • 10REN D, FEN G Q L, BOURRAT X. Effects of additives and templates on calcium carbonate mineralization in vitro [ J ]. Micron, 2011,42 (3) : 228 - 245.

引证文献1

;
使用帮助 返回顶部